Study on Wood Mechanical Properties of Bambusa wenchouensis

  • Received Date: 2005-11-08
  • Compared with Moso bamboo,Phyllostachys edulis,the wood mechanical properties of Bambusa wenchouensis,a sympodial bamboo,were studied.The result showed that its tensile strength parallel to grain(δt),compressive strength parallel to grain(δc),cleavage strength(C) and modulus of elasticity in static bending(MOE) were 238.0 MPa,75.1 MPa,45.6 N·mm-1 and 12.6 GPa respectively,which were larger than or almost equal to those of Moso bamboo.Its shearing strength parallel to grain(δs) and bending strength(MOR) were smaller.The wood mechanical properties of B.wenchouensis had good relativity with each other,and the δt∶δc∶δs∶C∶MOR was equal to 3.2∶1.0∶0.2∶0.6∶1.8.This study could lay theoretical foundation for proper exploiture and utilization of B.wenchouensis.
  • 加载中
  • [1] 潘孝政. 大木竹及其栽培

    [J]. 竹子研究汇刊, 1993, 12 (3) : 70~74

    [J]. 竹子研究汇刊,1984, 3 (2) : 92~100

    [4] 林景献. 大木竹的生长与营林技术调查

    [5] 中国标准出版社第一编辑室. 木材工业标准汇编

    [M]. 北京:中国标准出版社, 2002: 207~228

    [7] 俞友明,杨云芳,方伟,等. 红壳竹人工林竹材物理力学性质的研究

    [J]. 竹子研究汇刊, 2001, 20 (4) : 42~46

    [9] 於琼花,俞友明,金永明,等. 雷竹人工林竹材物理力学性质

    [J].浙江林学院学报, 2004, 21 (2) : 130~133

    [11] 王传贵,柯曙华,杨强. 黄山松木材物理力学性质研究

    [J]. 安徽农业大学学报, 1997, 24 (4) : 388~390

    [13] 林金国,郑郁善,张金泮. 福建含笑木材物理力学性质的研究

    [J]. 西北林学院学报, 1999, 14 (2) : 33~36

    [J]. 西南林学院学报, 1998, 18 (3) : 189~193

    [16] 张宏健,杜凡,张福兴. 云南4种材用丛生竹的主要物理力学性质

    [J]. 竹子研究汇刊, 1999, 18 (1) : 58~62

    [18] 林金国,何水东,林顺德,等. 麻竹材基本密度与力学性质变异规律的研究

    [19] 陈祖松. 福建柏人工林木材物理力学性质的试验研究

    [J]. 福建林学院学报, 1999, 19 (3) : 223~226

    [21] 王桂岩,王彦,李善文,等. 13种杨树木材物理力学性质的研究

    [J]. 山东林业科技, 2001 (2) : 1~11

    [J]. 林业科学研究, 1994, 7 (3) : 259~262

    [24] 骆秀琴,管宁,张寿槐,等. 32个杉木无性系木材密度和力学性质的变异

    [25] 尹思慈. 木材学

    [M]. 北京:中国林业出版社, 2001: 171

    [27] 苏文会,顾小平,岳晋军,等. 大木竹秆形结构的研究

    [J]. 林业科学研究, 2006, 19 (1) : 98~101

    [J]. 林业科学研究, 2005, 18 (3) : 250~254

    [30] 苏文会,顾小平,马灵飞,等. 大木竹纤维形态与组织比量的研究

    [31] 苏文会,顾小平,马灵飞,等. 大木竹化学成分的研究

    [J]. 浙江林学院学报, 2005, 22 (2) : 180~184

  • 加载中
通讯作者: 陈斌, bchen63@163.com
  • 1. 

    沈阳化工大学材料科学与工程学院 沈阳 110142

  1. 本站搜索
  2. 百度学术搜索
  3. 万方数据库搜索
  4. CNKI搜索

Article views(3835) PDF downloads(2874) Cited by()

Proportional views

Study on Wood Mechanical Properties of Bambusa wenchouensis

  • 1. Research Institute of Subtropical Forestry,CAF,Fuyang 311400,Zhejiang,China
  • 2.  International Center for Bamboo and Rattan,Beijing 100102,China
  • 3. School of Engineering,Zhejiang Forestry College,Lin'an 311300,Zhejiang,China
  • 4. International Center for Bamboo and Rattan,Beijing 100102,China

Abstract: Compared with Moso bamboo,Phyllostachys edulis,the wood mechanical properties of Bambusa wenchouensis,a sympodial bamboo,were studied.The result showed that its tensile strength parallel to grain(δt),compressive strength parallel to grain(δc),cleavage strength(C) and modulus of elasticity in static bending(MOE) were 238.0 MPa,75.1 MPa,45.6 N·mm-1 and 12.6 GPa respectively,which were larger than or almost equal to those of Moso bamboo.Its shearing strength parallel to grain(δs) and bending strength(MOR) were smaller.The wood mechanical properties of B.wenchouensis had good relativity with each other,and the δt∶δc∶δs∶C∶MOR was equal to 3.2∶1.0∶0.2∶0.6∶1.8.This study could lay theoretical foundation for proper exploiture and utilization of B.wenchouensis.

Reference (32)

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return